Mechanical Properties:
– 060A35 steel grade has a tensile strength of 580-680 MPa.
– It has a yield strength of 345 MPa.
– The elongation at break is about 18%.
– 060A35 steel grade has good toughness, making it suitable for applications requiring high strength and impact resistance.
– It has moderate hardness, with a Brinell hardness range of 170-260 HB.
Technical Properties:
– 060A35 steel grade has a good machinability, allowing it to be easily processed and formed into various shapes.
– It has good weldability, enabling it to be joined by various welding methods such as arc welding and spot welding.
– This steel grade can be heat treated to improve its strength and hardness.
Chemical Composition:
– The chemical composition of 060A35 steel grade typically consists of:
– Carbon (C): 0.32-0.39%
– Silicon (Si): 0.10-0.35%
– Manganese (Mn): 0.50-0.80%
– Phosphorus (P): Maximum 0.050%
– Sulfur (S): Maximum 0.050%
– Other elements such as copper (Cu), chromium (Cr), and nickel (Ni) may be present in trace amounts.
Applications:
– Due to its high tensile strength and moderate hardness, 060A35 steel grade finds applications in various industries, including:
– Automotive manufacturing: It can be used in the production of gears, shafts, and other components that require high strength and durability.
– Construction: It is suitable for structural applications such as beams, columns, and brackets.
– Machinery manufacturing: 060A35 steel grade can be used for manufacturing machine parts like bolts, nuts, and axles.
– Toolmaking: It is often utilized in the production of tools and dies.
Note: The specific mechanical properties, technical properties, and chemical composition may vary slightly depending on the manufacturer and production process. It is always recommended to refer to the manufacturer’s specifications for precise details.